ABRASOHARD 610

Specification

Description

• ABRASOHARD 610 is a low hydrogen type electrode for hardsurfacing repair of high carbon and alloy steel parts for multi-layer welding bead.
• Corrosion resistant due to high chromium content deposit 
• Minimum spatter
• Stable arc
• Easy slag detachment

Application

• Rebuilding and repair of sugar mill cane knives, hammers, compactors, pump housings, paper breaker rolls, asphalt mixer paddles, dredge cutters, grader blades, grader end bits, dredge pump impellers, bucket lips and teeth, rolls, and crusher jaws

 

Technical Data

TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C	Si	Mn	Cr	Mo
0.60	1.00	0.30	8.80	5.50

 

HARDNESS OF WELD METAL:

Hardness	Vickers (Hv)	Rockwell (HRC)
First Layer	530 - 560	51 - 53
Second Layer	550 - 620	52 - 56
Third Layer	620 - 700	56 - 60

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (-)

DIAMETER (mm)	3.2	4.0	5.0	6.0
LENGTH (mm)	350	400	400	450
Current Amp	90 - 130	120 - 180	170 - 230	210 - 280

Welding Positions:	FLAT, VERTICAL UP, OVERHEAD
Approvals:	N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.