NHF-950

Specification

AWS Specification: N/A
JIS Specification: DFWA-700S
Other Specification: N/A

Description

Application

Remarks

  • Preheat over 200ºC and postheat at 500-600ºC
  • Underlaying with low hydrogen type electrodes (N-7016 or N-7018) is required
  • Dry the electrodes at 150-200ºC for 30-60 minutes before use
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    Cr

    B W

    2.78

    0.29

    3.22

    0.10

    0.12 47.30

     

    HARDNESS OF WELD METAL:
    Hardness
    Vickers (Hv)
    Rockwell (HRC)

    Value

    700 - 950

    62 - 64

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    350

    Current Amp

    90 - 130

    120 - 180

    170 - 230


    Welding Positions: FLAT, FILLET, VERTICAL UP, OVERHEAD, HORIZONTAL
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.