NIDURIT 65

Specification

AWS Specification: N/A
JIS Specification: N/A
Other Specification: DIN 8555: E10-UM-65-GRZ

Description

Application

Remarks

  • Hold electrode as vertically as possible
  • Keep a short arc
  • Reduce dilution with the base metal by weaving
  • For multi-pass applications, a cushion layer with NSS-307 is recommended
  • Re-dry electros that have gotten damp at 200ºC for 2 hours
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    Cr

    Mo Nb W V

    4.50

    1.00

    0.21

    23.50

    6.50 5.50 2.20 1.50

     

    HARDNESS OF WELD METAL:
    Hardness
    Vickers (Hv)
    Rockwell (HRC)

    Value

    800 - 900

    64 - 67

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    350

    Current Amp

    110 - 150

    140 - 200

    190 - 250


    Welding Positions: FLAT, OVERHEAD, HORIZONTAL
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.