NSS-308L-15

Specification
AWS Specification: AWS A5.4 E308L-15
JIS Specification: D308L-15
Other Specification: N/A
Description
  • NSS-308L-15 is a lime-titania formula designed for welding of AISI types 301, 302, and 304 stainless steel
  • Welds are porosity free with corrosion resistance comparable to that of base metal

 

TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

Ni

0.03

0.41

1.67

20.60

9.50

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 

434  (63)

550 (80)

44

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

300

350

350

350

Current Amp

Flat

50 - 80

70 - 110

100 - 150 

130 - 180

Vertical & Overhead

45 - 75

65 - 105

95 - 140

-


Welding Positions: ALL POSITIONS 
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Keep the arc length as short as possible
  • Welding current used should be as low as possible
  • DC (+) current is recommended for welding
  • Welding of AISI types 301, 302, and 304 stainless steel