NSS-410NiMo

Specification
AWS Specification: AWS A5.4 E410NiMo-16
JIS Specification: N/A
Other Specification: N/A
Description
  • NSS-410NiMo is designed for surfacing of carbon steel to resist heat, corrosion, erosion, and abrasion

 

TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

Ni

Mo

0.043

0.27

0.33

12.18

4.52

0.068

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 

917  (133)

18

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

300

350

350

350

Current Amp

Flat

50 - 80

70 - 110

100 - 150

130 - 180

Vertical & Overhead

45 - 75

65 - 105

95 - 140

-

 

Welding Positions: FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Pre-heat at 200 - 400C as weld metal has self-hardening properties
  • Post-heat at 700-800C in order to improve the structure and to stress relieve after welding
  • For welding of 13% Cr steel