NHF-WH2

Specification
AWS Specification: N/A
JIS Specification: N/A
Other Specification: DIN 8555: E2-UM-60-S
Description
  • NHF-WH2 is a heavily coated lime titania electrode intended for welding tools of water hardening, carbon, or low alloy steels
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

B V

0.60

0.40

0.60

0.40

0.80 0.25

 

HARDNESS OF WELD METAL:
Hardness
Vickers (Hv)
Rockwell (HRC)

Value

700 - 800

60 - 64

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

3.2

4.0

5.0

LENGTH (mm)

350

350

350

Current Amp

90 - 130

120 - 180

170 - 230


Welding Positions: FLAT, FILLET, VERTICAL UP
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Trimming dies for hot and cold work
  • Thread cutting tools
  • Cold heating dies
  • Wood working tools
  • Cold punches
  • Deep drawing
  • Impact extension
  • Embossing tools

about us

Industrial Welding Corporation (IWC) was established in 1982 by Mr. H. Ong Hai who had 25 years of welding industry experience (at that time). Since then, IWC has consistently and successfully earned an excellent ...
Copyright © 2018 Industrial Welding Corporation
Web Design By WebToGo Philippines