NIDURIT 60

Specification
AWS Specification: AWS A5.13 EFeCr-A1
JIS Specification: N/A
Other Specification: DIN E10-UM-600-GRZ
Description
  • NIDURIT 61 is a low hydrogen hardfacing electrode against abrasion and pressure and moderate impact loads
  • High efficieny with 165% metal recovery
  • Contains chromium carbide as alloying elements
  • Weld seam is noted for its extremely finely rippled beads and easy slag removal
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

Fe

3.20

1.00

0.15

29.00

Bal.

 

HARDNESS OF WELD METAL:
Hardness
Vickers (Hv)
Rockwell (HRC)

Value

660 - 700

58 - 60

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

3.2

4.0

5.0

LENGTH (mm)

350

350

350

Current Amp

90 - 130

120 - 180

170 - 230


Welding Positions: FLAT, FILLET, VERTICAL UP, OVERHEAD, HORIZONTAL
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Conveyor screws
  • Excavaotr bucket teeth
  • Sand and slurry pumps
  • Mixer paddles
  • Maintain a short arc
  • Do not buffer the passes too thick
  • Peen the weld thoroughly on stress prone workpieces
  • Preheating is generally not required
  • With Mn steels, use the lowest amperage possible

about us

Industrial Welding Corporation (IWC) was established in 1982 by Mr. H. Ong Hai who had 25 years of welding industry experience (at that time). Since then, IWC has consistently and successfully earned an excellent ...
Copyright © 2018 Industrial Welding Corporation
Web Design By WebToGo Philippines