SHIELD METAL ARC WELDING (SMAW)

 Printer Friendly Layout

N-8018-C3

Specification
AWS Specification: AWS A5.5 E8018-C3
JIS Specification: N/A
Other Specification: N/A
Description
  • N-8018-C3 is a 1% nickel, low hydrogen, iron powder electrode used for welding high strength steels in the 70-80,000 PSI tensile strength range
  • Offers high deposition efficiency, producing excellent quality of weld weld deposits with good impact properties even at temperatures as low as -60°C
  • Used for fillet welds on high strength quenched and tempered steels such as ASTM A514 and A517
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Ni

0.07

0.45

0.91

1.03

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

530 (77)

600 (87)

31

-40°, 60  (-40°, 44)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+), DC (-)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

350

350

400

400

Current Amp

Flat

65 - 90

90 - 130

135 - 185

190 - 250

Vertical & Overhead

60 -90

80 - 120

110 - 170

160 - 210

Welding Positions: ALL POSITIONS 
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Cor-ten, Mayari R, LT75, N-A-Z High Tensile, V-55, Yoloy HS, military, and commercial applications
  • Dry the electrodes at 350-400°C for about one hour before use
  • Store the electrodes at 100-150°C after drying to keep away from moisture
  • Adopt back step method or strike the arc on a small steel plate to prevent blowholes at the arc starting
  • Keep the arc as short as possible
  • Pre-heat at 100-150°C