SHIELD METAL ARC WELDING (SMAW)

 Printer Friendly Layout

N-9018-G

Specification
AWS Specification: AWS A5.5 E9018G
JIS Specification: D5816
Other Specification: N/A
Description
  • N-9018-G is an iron powder low hydrogen type electrode for all-position welding that provides good notch toughness of weld metal at low temperature
  • Good usability and X-ray soundness of weld metal 
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

 Ni Cr Mo

0.07

0.40

1.40

0.023

0.012

 1.17 0.07 0.18

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J 
 

570 (83)

660 (96)

28

-20°, 160 

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+), DC (-)

DIAMETER (mm)

2.6

3.2

4.0

5.0

LENGTH (mm)

350

350

400

400

Current Amp

Flat

55 - 85

90 - 130

135 - 185

190 - 250

Vertical & Overhead

50 - 80

80 - 120

110 - 170

-

Welding Positions: ALL POSITIONS INCLUDING VERTICAL DOWN
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Welding of 60 kgf/mm2 class high tensile strength steel for pressure vessels, penstocks, bridges offshore constructions, vehicles and machinery

  • Dry the electrodes at 350-400°C for about one hour before use
  • Store the electrodes at 100-150°C after drying to keep away from moisture
  • Adopt back step method or strike the arc on a small steel plate to prevent blowholes at the arc starting
  • Keep the arc as short as possible
  • Pre-heat at 100-150°C