SHIELD METAL ARC WELDING (SMAW)

 Printer Friendly Layout

N-10016-D2

Specification
AWS Specification: AWS A5.5 E10016-D2
JIS Specification: N/A
Other Specification: N/A
Description
  • N-10018-D2 is a high quality electrode designed for high tensile steels and manganese-molybdenum steels
  • Coating is specially formulated to resist moisture pick-up under conditions of high heat and humidity
  • An electrode with high operator appeal
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Mo

0.12

0.41

1.96

0.39

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
PWHT
 

630 (91)

735 (107)

24

620°C x 1 hr

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

350

350

400

400

Current Amp

Flat

55 - 85

90 - 130

140 - 190

190 - 240

Vertical & Overhead

50 - 80

75 - 115

100 - 160

-

Welding Positions: ALL POSITIONS
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Applications requiring at least 100,000 psi tensile strength, good ductility, and crack resistance
  • Manganese-moly castings
  • Alloy forgings structures
  • Pressure vessels applications in either the as welded or stress relieved conditions
  • Dry the electrodes at 350-400°C for about one hour before use
  • Store the electrodes at 100-150°C after drying to keep away from moisture
  • Adopt back step method or strike the arc on a small steel plate to prevent blowholes at the arc starting
  • Keep the arc as short as possible
  • Pre-heat at 100-150°C