SHIELD METAL ARC WELDING (SMAW)

 Printer Friendly Layout

N-7010-A1

Specification
AWS Specification: AWS A5.5 E7010
JIS Specification: N/A
Other Specification: N/A
Description
  • N-7010-A1 is a high cellulose electrode specifically designed for vertical down welding of all passes on high tensile pipe
  • These electrodes are characterized by a steady, forceful, concentrated arc to ensure good penetration and wetting action
  • The slag is fast freezing, minimizing slag interference, and allows for easy control of the weld shape and size
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Mo

0.09

0.14

0.43

0.49

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
PWHT
 

440  (64)

550  (80)

29

-620°C x 2 hrs.

 

SIZE AND RECOMMENDED CURRENT RANGE: DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

350

350

400

400

Current Amp

Flat

50 - 75

70 - 110

110 - 155

155 - 200

Vertical & Overhead

30 - 70

55 - 105

90 - 140

140 - 180

 

Welding Positions: ALL POSITIONS 
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • N-7010-A1 is most suited for the welding of long distance pipe lines
  • Designed for use on carbon moly piping used in high pressure, high temperature steam service, structural shape, plates or castings where the molybdenum content is approximately 0.50%.  
  • Appropriate for welding higher strength carbon and low alloy steels with tensile strength of 83.0 KSI 
  • May also be used to join some dissimilar Cr-Moly steels of high alloy content to those of lower alloy content
  • The root pass is deposited in the vertical down position
  • A drag technique is used and the electrode is pressed tightly into the joint
  • The second or hot pass should be deposited as soon as possible after the root pass
  • The current should be high enough to burn out any possible wagon tracks or slag A slight weaving technique is usually employed
  • The filler passes are applied using a weaving technique in order to completely fill the joint
  • Excessive travel speed should always be avoided to lessen any chance of porosity.
  • Pre-heat and interpass temperatures between 300ºC and 400ºC are recommended