ABRASOHARD 610

Specification
AWS Specification: N/A
JIS Specification: N/A
Other Specification: N/A
Description
  • ABRASOHARD 610 is a low hydrogen type electrode for hardsurfacing repair of high carbon and alloy steel parts for multi-layer welding bead.
  • Corrosion resistant due to high chromium content deposit 
  • Minimum spatter
  • Stable arc
  • Easy slag detachment
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

Mo

0.60

1.00

0.30

8.80

5.50

 

HARDNESS OF WELD METAL:
Hardness
Vickers (Hv)
Rockwell (HRC)

First Layer

530 - 560

51 - 53

Second Layer 550 - 620 52 - 56
Third Layer 620 - 700 56 - 60

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (-)

DIAMETER (mm)

3.2

4.0

5.0

6.0

LENGTH (mm)

350

400

400

450

Current Amp

90 - 130

120 - 180

170 - 230

210 - 280

Welding Positions: FLAT, VERTICAL UP, OVERHEAD
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Rebuilding and repair of sugar mill cane knives, hammers, compactors, pump housings, paper breaker rolls, asphalt mixer paddles, dredge cutters, grader blades, grader end bits, dredge pump impellers, bucket lips and teeth, rolls, and crusher jaws

 